A two component, semigloss polyurethane paint, hardener aliphatic isocyanate.
Recommended as a semigloss topcoat for epoxy and polyurethane systems exposed to weathering and/or chemical stress.
Recommended for painting of transport and haulage equipment, storage tank exteriors, steel framework and other steel structures, machinery and equipment.
- Features: Excellent weathering and abrasion resistance. A durable, easy to clean and non-chalking topcoat with good gloss and colour retention. The product has MED (Marine Equipment Directive) certificate no VTT-C-4033-15-09 and is thus accepted for painting surfaces inside the ships.
- Colour Cards: RAL, NCS, SSG, BS, MONICOLOR NOVA and SYMPHONY colour cards. TEMASPEED tinting.
- Gloss groups: Semi-gloss
- Thinner: 1048, 1067 and 1061
- Mixing ratio: Base 5 parts by volume 506-series, Hardener 1 part by volume 008 7590
- Application method: By airless or conventional spray or by brush.
- Pot-life (+23°C): 4 hours
- Solids volume: 56 ± 2 % volume % (ISO 3233), 70 ± 2 % weight %
- Density: 1.3 ± 0.1 kg / l (mixed)
- Product code: 506-series
- MED Certificate: PDF
|Recommended film thicknesses||Theoretical coverage|
|40 µm||70 µm||14.0 m2/l|
|60 µm||110 µm||9.3 m2/l|
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
|DFT 50 um||+ 5 °C||+ 10 °C||+ 23 °C||+ 35 °C|
|Dust dry, after||45 min||30 min||15 min||10 min|
|Touch dry, after||8 h||6 h||4 h||2½ h|
|Recoatable, after||No limitations.|
Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
All surfaces must be dry. The temperature of the ambient air, surface or paint should not fall below + 5 ºC during application or drying. Relative humidity should not exceed 80 %. The surface temperature of the steel should remain at least 3 ºC above the dew point.
Primed surfaces: Oil, grease, salt and dirt are removed from the surface by appropriate means. Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4)
Temacoat GPL-S Primer, Temacoat GF Primer, Temacoat HB Primer, Temacoat PM Primer, Temacoat GPL-S MIO, Temacoat SPA, Temacoat RM 40, Temamastic PM 100, Temabond, Temadur 20, Temadur Primer, Temaprime GF, Fontecoat EP Primer and Fontecryl 10.
Temadur and Temathane
By airless or conventional spray or by brush. In order to obtain an even, non-porous finish at the airless spray application the viscosity should be 30 - 60 s DIN4. Depending on the temperature of the components (base, hardener, thinner) and the required viscosity the paint should be thinned 10 - 23 %. Airless spray nozzle tip 0.011" - 0.017" and nozzle pressure 120 - 160 bar. Spray angle shall be chosen according to the shape of the object. At brush application the paint should be thinned according to the circumstancies.
Mixing of components
First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use. Use Temaspeed Squirrel Mixer for mixing.
Cleaning of tools
Thinner 1048, 1067 or 1061
EU VOC 2004/ 42/EC-limit value
The Volatile Organic Compounds amount is 420 g/litre of paint mixture.
VOC content of the paint mixture (thinned 23 % by volume) is 495 g/l. Only for industrial use.
Health and safety classification
Containers are provided with safety labels, which should be observed. Further
information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oyj.